seo

Alumina Polyurethane Foam Filter The factors affecting the quenching temperature of the Alumina Polyurethane Foam Filter in the roller kiln were compared. The relationship between the height of the flame shield, the residual heat pressure, the size of the product and the quenching fan and the quenching temperature were compared in turn, and the reasons […]

Alumina Foam Ceramics Foundry Filter Alumina Foam Ceramics Foundry Filter is sintered by energy saving and environmentally friendly roller kiln. Combined with the sintering characteristics of the foam ceramic filter plate, the specific parameters of the roller kiln were established. For example, the ratio of the length of the pre-tropical zone of the roller kiln, […]

Ceramic Honeycomb Filter For Metal Melting Preparation of zirconia foam ceramics, adding zirconia ceramic powder and stirring evenly, then adding curing agent. After thorough mixing, it is placed in a molding container for reaction curing, and the cured foamed ceramic sponge is treated by opening. After sintering at a high temperature, a zirconia foam ceramic […]

High Thermal Shock Resistance Zirconia Foam Ceramic Filter Development and application results of MgO partially stabilized ZrO2 foam ceramics. The sintering temperature of the MgO-ZrO2 foam ceramic is 1730-1760 °C. Cooling at 300 ° C / h after sintering allowed the t-ZrO 2 precipitated particles to remain at room temperature. Aging at 1100 ° C […]

Zirconia Foam Ceramic Filter Zirconia Foam Ceramic Filter was prepared by organic foam impregnation method, and the effects of various process factors on the properties of foam ceramics were investigated. The phase composition and microstructure of foam ceramics were analyzed and discussed by XRD and SEM. When the mass fraction of the dispersant tetramethylammonium hydroxide […]

Zirconia Foam Ceramic Filter For Aluminium Foundry The effect of CeO2 on the properties of alumina-based foam ceramic filters was investigated using an organic foam impregnation process. The microstructure of the sample was investigated by scanning electron microscopy (SEM) by measuring the normal temperature compressive strength, thermal shock stability, permeability and other properties of the […]

Ceramic Foam Filter Used In Metallurgy And Casting The foam ceramic filter was prepared by organic foam impregnation process. Effect of additive SiO2 micropowder and CeO2 on SiC-alumina-based foam ceramic filter. The orthogonal experiment was carried out and the performance of ceramics was tested. The results show that there is an optimal ratio between the […]

Cordierite Ceramic Foam Filter The main application of Cordierite Ceramic Foam Filter is as a molten metal filter, but currently the filters on the market generally have the disadvantages of low bending strength and poor thermal shock stability. Therefore, research on high performance foam ceramics has obvious engineering significance and application value. Foamed ceramics were […]

Metal Filtration The ceramic filter for aluminium Metal Filtration was prepared by an organic foam impregnation process, and the effect of sintering temperature on the performance of the alumina-based ceramic foam filter. When the sintering temperature is 1430 ° C, the two properties are higher. At this time, due to the uniform grain size, less […]

Alumina Carbide Ceramic Foam Filter Melting at 700-750 °C, using a multi-stage degassing purification system to degas the melt, using 30ppi foam ceramic filter plate to filter the melt. The aluminum alloy ingot is obtained by melt casting, and the stress relief treatment is carried out at 300-500 ° C for ≥ 1 hour. The […]